YAPIFINE® CURE ACR

Acrylic resin based curing material, applied on freshly poured concrete; retains the water on concrete thanks to film layer it creates and prevents rapid loss of water, as well as shrinkage and cracking.

Request Product Information

Technical profile

Material data,
at a glance.

Key properties and declared technical characteristics for product selection and initial evaluation.

Appearance: White liquid pH 7 - 9
Structure: Acrylic Copolymer Based Drying Time 2 hours
Application Temperature: Between +5°C and +30°C Service Temperature -20°C / +70°C
Density: 1 kg/L ± 0,03

Performance

Product advantages

Economic and effective curing agent.
Applicable with brush, roll or spray.
Film layer detains sufficient humidity necessary for complete hydration of cement in order to obtain required concrete strength.
Prevents formation of shrinkage and cracks.
Dust-free; ensures more solid surface.
All applications with cement or resin basis can be made on cured surfaces.

Application range

Areas of use

Indoor and outdoor spaces
For curing horizontal and vertical construction elements
Airports and field concrete
Channel concrete
Floor-hardening applications
While pouring concrete in areas with low humidity and high evaporation and airstream

Use guidance

From selection
to application.

Application

YAPIFINE CURE ACR is ready to use. Shake before using. Can be applied by a roller or a spraying machine onto freshly poured concrete. If second layer application is required; second layer should be applied 6 hours after the first layer application. In case of a roller application it should be applied as a thin layer. The material should be evenly distributed all throughout and it should be made sure that pooling does not occur.

Specification & supply

Standards, formats
and handling.

Packaging

30 kg plastic drum
210 kg barrel

Storage

The shelf life of the product is 12 months when it is stored on wooden pallets in a cool, dry and moisture free environment with an ambient temperature between +5°C and +25°C.