YAPIFINE BASE® EPOXY POWER

Epoxy based, two component, solvent free and low viscosity self levelling floor coating with high chemical and physical strength.

Request Product Information

Technical profile

Material data,
at a glance.

Key properties and declared technical characteristics for product selection and initial evaluation.

Colour: Grey / White / RAL Colours Flexural Strength 25 N/mm²
Density (+20°C): 1.54 g/cm³ ± 0.02 Compressive Strength ≥ 45 N/mm²
Mixture Ratio: 3,8 / 1 (A component / B component) Adhesive Strength to Concrete ≥ 4 N/mm²
Appearance: Glossy Adhesive Strength to Metal ≥ 3 N/mm²
Pot Life (+20°C): 30 minutes Abrasion Resistance by Taber Abraser 70 mg
Drying Period (at +23°C, 55% relative humidity): Drying time: 10 hours Time for new coat: 8-24 hours Through-dry time: 7 days Hardness (Shore D) (7 days) 76
Permeability to Water Vapour: Class 1
Capillary Water Absorpsion: ≤ 0,5 kg/(m².h0,5)
Temperature Resistance: 121°C dry Permeability to CO2 Sd > 50
Application Temperature: +10°C ile +30°C Reaction to Fire E

Performance

Product advantages

High chemical strength against alkali, dilute acid, sewage, water, oil products, mineral oils and fuels.
High mechanical strength and abrasive strength.
Provides good film after curing. Creates joint-free surface.
Easy to clean thanks to smooth surface.
Easy to apply.

Application range

Areas of use

Indoor and outdoor spaces
Food production and storage facilities
Shopping malls and supermarkets
Areas subject to light-medium industrial loads
Sewage and waste plants
Parking lots, walking trails
Pulp and paper factories
Refineries, warehouses and factories

Use guidance

From selection
to application.

Application

The product should be poured on to the surface and spread by a notched trowel. For the better finishing result, turn the notched trowel and smoothen the surface. To obtain an even thicknees and get rid of entrained air. 5 minutes after application use the spiked roller in two directions perpendicular to each other. This is especially necessary when the coating has been filled with silica sand. Wait for minimum 4 days before taking into service. Do not keep the equipments in use for more than 40 minutes in the mixture; in case of delay, wash equipments with epoxy thinner. Even though YAPIFINE BASE EPOXY POWER is solvent free, proper ambient ventilationn will help protect the operator, prevent condensation on paint film and ensure optimum coating performance. Ventilation should continue during curing as well.

Specification & supply

Standards, formats
and handling.

Packaging

Tin buckets set of 19 kg + 5 kg set

Storage

The shelf life of the product is 12 months when it is stored on wooden pallets in a cool, dry and moisture free environment with an ambient temperature between +10°C and +25°C. The opened material should be used as soon as possible.